1

Nominal thickness

μm

GB/T 13542.2-2009

317

2

Thickness deviation

/

±10%

3

Nominal Weight

g/m2

GB/T 13542.2-2009

435

4

Weight deviation

/

-5%,+10%

5

Width deviation

mm

GB/T 13542.2-2009

-0+5

6

Tensile strength

MD

MPa

GB/T 13542.2-2009

≥100

TD

MPa

≥100

7

Elongation at break

MD

%

≥100

TD

%

≥80

8

Heat shrinkage

MD

%

GB/T 13542.2-2009

≤0.8

TD

%

≤0.6

9

Coating adhesion

EVA Side

级

GB/T 9286-1998

0

10

Boiling

watertreatment (boil for 24h)

Appearance

/

GB/T 17748-2008

No delamination ，

no bubble ,no peeling

Coating adhesion

- GB/T 9286-1998

0 Grade

Grade

GB/T 9286-1998

0

11

Peeling strength with EVA(Initial)

Transparent EVA

N/cm

GB/T 2790-1995

≥50

12

Peeling strength with silica gel

N/cm

GB/T 1040-2006

≥20

13

（ 400-1000nm ）

transmittance

%

GB/T 2410-2008

≥85

14

Breakdown voltage

KV

GB/T 13542.2-2009

≥17

15

Partial Discharge

VDC

IEC 60664-1-2007

≥1500

16

DTI

μm

IEC TS 62788-2:2017

≥300

17

Moisture vapor transmission rate

38℃*90RH%

g/m²•d

GB/T 21529-2008

≤2.0

18

PCT aging treatment(121℃, 2 ato,

48h)

△b

GB/T 13542.2-2009

△b≤2.0

≥30%

19

Damp Heat (1000h)

UV Aging (120kwh)

Thermalcycle(200)

Humidity-freeze (10)

△b

IEC 61215-2005

No brittle fracture, blistering, delamination

△b≤2.0